关键词：纳米片状NiO;葡萄糖;电化学传感器;水热法
摘要：
以聚乙二醇为表面活性剂，采用水热法制备纳米片状NiO，并用于电化学检测葡萄糖。通过X射线衍射（XRD）和透射电镜（TEM）分别对所得产物的结构和形貌进行表征。TEM结果表明，所得产物为超薄片状结构NiO，其大小在50nm左右。采用循环伏安法（CV）研究纳米片状NiO修饰电极在NaOH溶液中的电化学行为。结果表明，该电极对葡萄糖具有良好的电催化氧化性能，它对葡萄糖响应的线性范围为2.5810-6~7.7110-3 mol/L，检出限为0.5 mol/L（S/N=3）。
Preparation of NiOnanoflake by hydrothermal method and its electrochemical detection of glucose
HUANG Man, CHEN Yun
Nanjing Vocational Institute of Science and Technology, Nanjing 210048, China
Abstract: NiOnanoflake was prepared by hydrothermal method using polyethylene glycol as surfactant and used for electrochemical detection of glucose.The structure and morphology of the as-prepared products were characterized by X-ray diffraction(XRD) and transmission electron microscope(TEM).The TEM images showed that the synthesized NiO was ultrathin nanoflake with size about 50nm.The electrochemical behavior of NiOnanoflake in NaOH solution were studied by cyclic voltammetry(CV).The results show that the electrode exhibits good electrocatalytic activity toward the oxidation of glucose.The linear range for the determination of glucose is 2.58×10-6-7.71×10-3mol/L with a detection limit of 0.5 μmol/L(S/N=3).
Keywords: NiOnanoflake;glucose;electrochemical sensor;hydrothermal method
2016, 42(11): 44-47 收稿日期: 2016-5-9;收到修改稿日期: 2016-5-9
基金项目:
作者简介: 黄曼(1981-),女,江苏南京市人,实验师,硕士,研究方向为化工产品分析与检验、分析化学教学工作。
参考文献
[1] BAI G,DAI H,Deng J,et al.Porous NiOnanoflowers and nanourchins:highly active catalysts for toluene combustion[J].CatalCommun,2012,27:148-153.
[2] LI G J,HUANG X X,SHI Y,et al.Preparation and characteristica of nanopcrystallineNiO by organic solvent method[J].Mater Lett,2001,51:325-330.
[3] SONG X,GAO L.Facile synthesis of polycrystalline NiOnanorods assisted by microwave heating[J].J.Am.Ceram.Soc,2008,91:3465-3468.
[4] PANG H,LU Q,LI Y,et al.Facile synthesis of nickel oxide nanotubes and their antibacterial,electrochemical and magnetic properties[J].ChemCommun,2005:7542-7544.
[5] WANG D,SONG C,HU Z,et al.Fabrication of hollow spheres and thin films of nickel hydroxide and nickel oxide with hierarchical structures[J].J.Phys.Chem.B,2005,109:1125-1129.
[6] LIM S H,WEI J,LIN J,et al.A glucose biosensor based on electrodeposition of palladium nanoparticles and glucose oxidase ontoNafion-solubilized carbon nanotube electrode[J].Biosens.Bioelectron,2005,20:2341.
[7] LI Y,SONG Y Y,YANG C,et al.Hydrogen bubble dynamic template synthesis of porous gold for nonenzymatic electrochemical detection of glucose,Electrochem[J].Commun,2007,9:981-988.
[8] HWANG S G,KIM G O,YUN S R,et al.NiO nanoparticles with plate structure grown on graphene as fast charge-discharge anode material for lithiumion batteries[J].Electrochim.Acta,2012,78:406-411.
[9] MU Y,JIA D,HE Y,et al.Nano nickel oxide modified non-enzymatic glucose sensors with enhanced sensitivity through an electrochemical process strategy at high potential[J].Biosens.Bioelectron,2011,26:2948-2952.
[10] WANG G,LU X,ZHAI T,et al.Free-standing nickel oxide nanoflake arrays:synthesis and application for highly sensitive non-enzymatic glucose sensors[J].Nanoscale,2012(4):3123-3127.
[11] DING Y,LIU Y,PARISI J,et al.A novel NiO-Au hybrid nanobelts based sensor for sensitive and selective glucose detection[J].Biosens.Bioelectron,2011,28:393-398.
[12] ZHANG Y,XU F,SUN Y,et al.Assembly of Ni(OH)2nanoplates on reduced graphene oxide:a two dimensional nanocomposite for enzyme-free glucose sensing[J].J.Mater.Chem.,2011,21:16949-16954.