作者：蔡力勋, 贾琦, 包陈
作者单位：西南交通大学力学与工程学院, 四川 成都 610031
关键词：周向裂纹圆棒试样; 断裂韧性; 有限元分析; 规则化方法; 16Mn
摘要：
借助自制对中夹头和载荷分离法成功实现了周向裂纹圆棒试样的断裂韧性测试。基于有限元分析和柔度法得到了考虑弹性模量、试样直径、测试标距及裂纹深度等影响的统一裂纹长度预测公式;采用双引伸计测轴向位移、等面积法计算最终裂纹长度,解决了裂纹扩展偏心所带来的影响;有限元模拟分析证明了载荷分离理论适用于周向裂纹圆棒试样,并提出了几何函数G(a/R)的具体表达式;采用规则化方法获得了16Mn周向裂纹圆棒试样的JR阻力曲线。结果表明:由周向裂纹圆棒试样测得的结果与标准三点弯曲试样得到的结果接近,分散性小。
Study on testing fracture toughness of circumferentially-cracked round bars
CAI Li-xun, JIA Qi, BAO Chen
School of Mechanics and Engineering, Southwest Jiaotong University, Chengdu 610031, China
Abstract: In virtue of a self-invented centring clamp and load separation principle, the estimation for the fracture toughness of circumferentially-cracked round bar was carried out. On the basis of finite element analyses and compliance method, uniform formulas for crack length measurement are presented, in which the effect of elastic modulus, specimen diameter, gage length and crack depth is under consideration. In this paper, two extensometers are employed to measure axial displacement, the final crack length is determined by use of equivalent area method, and consequently, the effect of eccentricity of crack growth is eliminated. Finite element analyses confirm that the load separation principle is applicable for the circumferentially-cracked round bar, and then the detailed expression of geometry function for this specimen configuration is proposed. With normalization method, the JR curves of these specimens for 16Mn are obtained. The results show that the curves obtained by the circumferentially-cracked round bars are close to those by standard single edged notched bending(SEB) specimens.
Keywords: circumferentially-cracked round bar; fracture toughness; finite element analysis; normalization method; 16Mn
2012, 38(2): 6-9 收稿日期: 2011-9-22;收到修改稿日期: 2011-12-5
基金项目: 国家自然科学基金项目(11072205)
作者简介: 蔡力勋(1959-),男,山东曹县人,教授,博导,主要从事结构破坏与安全评定以及疲劳与断裂研究。
参考文献
[1] GB/T 21143-2007金属材料准静态断裂韧度的统一试验方法[S]. 北京:中国标准出版社,2007.
[2] Ibrahim R N, Stark H L. Establishing KIC from eccentrically fatigue cracked small circumferentially grooved cylindtrical specimens[J]. International Jornal of Fracture,1990(44):179-188.
[3] Lam Y C, Ibrahim R N. Improvement of the fracture toughness of an aluminum alloy[J]. Fatigue Fracture Engineering Materials and Structures,1944(17):277-284.
[4] Giovanola G H, Homma H, Lichtenberger M, et al. Fracture toughness measurements using smallcracked round bars[C]∥In Constraint Effects in Fracture:Theory and Applications. ASTM STP 1244. Philadelphia,1995:255-285.
[5] Hawley R H, Duffly H, Shih. Dynamic notched round bar testing[Z]. ASM Metals Handbook,1985:275-282.
[6] Costin L S, Duffy H, Freund L B. Fracture initiation in metals under stress wave loadinig conditions[C]∥Fast Fracture and Crack Arrest ASTM STP627. West Conshohocken,1977:301-308.
[7] Landes J D, Herrera R. A new look at J-R curve analysis[J]. International Journal of Fracture,1988(36):9-14.
[8] Sharobeam M H, Landes J D. The load separation criterion and methodology in ductile fracture mechanics[J]. International Journal of Fracture,1991(47):81-104.
[9] Benthem J P, Koiter W T. Asymptotic approximations to crack problems[C]∥Methods of Analysis and Solutions of Crack Problems. Groningen:Noordhoft International Publishing,1973:131-178.
[10] Li D M, Bakker A. Fracture toughness evaluation using circumferentially-cracked cylindrical bar specimens[J]. Engineering Fracture Mechanics,1997,57(1):1-9.
[11] Dzugan J, Viehrig H W. Application of the normalization method for the determination of J-R curves[J]. Materials Science and Engineering A,2004,387-389:307-311.
[12] Zhu X K, Joyce J A. J-resistance curve testing of HY80 steel using SE(B) specimens and normalization method[J]. Engineering Fracture Mechanics,2007(74):2263-2281.