作者：周洁, 毛汉领, 黄振峰, 曾德良

作者单位：广西大学机械工程学院, 广西南宁 530004

关键词：疲劳断裂; 声发射; 参数分析; 疲劳裂纹扩展

摘要：

疲劳断裂是金属结构的主要失效形式,通过金属疲劳断裂时声发射特征参数的提取,建立了声发射特征参数和裂纹扩展速率之间的关系,由试样的三点弯曲疲劳试验,证明采用声发射技术监测疲劳裂纹的扩展,不仅与疲劳裂纹扩展的变化规律相似,而且能实时的捕捉到疲劳裂纹的产生。

Acoustic emission technique for the detecting of metal fatigue fracture

ZHOU Jie, MAO Han-ling, HUANG Zhen-feng, ZENG De-liang

Guangxi University, Nanning 530004, China

Abstract: Fatigue fracture is the main style of failure in metal structure.To extract the features of the detected crack,two equations are cited to set up the correlation between AE parameters and crack propagation velocity.According to the experimental results of three-point bending specimen,acoustic emission techniques monitoring fatigue crack propagation is certificated not only to resemble variable rule of fatigue crack propagation,but also to catch generation of fatigue crack in real time.

Keywords: Fatigue fracture; Acoustic emission; Parameter analysis; Fatigue crack propagation

2007, 33(3): 7-9  收稿日期: 2006-11-14;收到修改稿日期: 2007-1-26

基金项目: 国家自然科学基金项目(50465002);广西自然科学基金项目(桂科基0448014)

作者简介: 周洁(1980-),女,硕士研究生,主要研究方向:机械设备状态监测与故障诊断、无损检测。

参考文献

[1] 吴清可.防断裂设计[M].北京:机械工业出版社,1995.
[2] 耿荣生,沈功田,刘时风.声发射信号处理和分析技术[J].无损检测,2002,24(1):23-28.
[3] 李庆芬,胡胜海.断裂力学及其工程应用[M].哈尔滨:哈尔滨工程大学出版社,2004,7:94-106.
[4] Roberts T M Talebzadeh M.Acoustic Emission Monitoring of Fatigue Crack Propagation[J].Journal of Constructional Steel Research,2003,59(6)::695-712.
[5] 田秀云,杜洪增,孙志强.金属材料疲劳裂纹扩展曲线拟合方法研究[J].工程力学,2003,20(4):136-140.
[6] 李光海,刘正义.基于声发射技术的金属高频疲劳监测[J].中国机械工程,2004,15(13):1205-1209