作者：刘勇, 杨光

作者单位：中国燃气涡轮研究院, 四川 绵阳 621703

关键词：荧光渗透检测;导向器;穿透性裂纹;过清洗

摘要：

导向器是飞机发动机上的重要零部件，发动机导向器在荧光渗透检测后，其叶片根部焊缝处存在穿透性裂纹漏检。为找出裂纹漏检原因，对裂纹形貌以及导向器结构进行观察，并结合渗透检测的原理进行分析，最终确定裂纹漏检的原因为导向器特殊结构导致的过清洗。通过进一步的试验，改进检测工艺，避免产生过清洗。通过对比可以看出，新工艺的使用，使导向器叶片的检测可靠性得到提高，降低漏检发生的概率。

Detection technology for through-wall cracks on guide vane

LIU Yong, YANG Guang

China Gas Turbine Establishment, Mianyang 621703, China

Abstract: Guide vane serves as a critical component of aeromotor. Some through-wall cracks at the root of vane were found failed to be examined after fluorescent penetrant inspection. To find out the reason, the crack form and guide vane structure were observed and analysis was carried out with the principle of penetrant testing. Finally, it was found it was the overwashing caused by the complex structure of guide vane that caused the missing inspection. In order to avoid overwashing, further experiment analysis and technology improvement were carried out, and these means were proved to be effective for improving the inspection reliability of guide vane and reducing the missing rate.

Keywords: fluorescent penetrant inspection;guide;through-wall cracks;overwashing

2017, 43(7): 40-43  收稿日期: 2016-12-08;收到修改稿日期: 2017-01-10

基金项目: 

作者简介: 刘勇(1964-),男,四川绵阳市人,技师,主要从事航空发动机零件的无损检测工作。

参考文献

[1] 廉筱纯,吴虎. 航空发动机原理[M]. 西安:西北工业大学出版社,2016.
[2] 陈光. 航空燃气涡轮发动机结构设计[M]. 北京:北京航空航天大学出版社,1988.
[3] 王自明. 航空无损检测综合知识[M]. 北京:国防工业出版社,2016.
[4] 任学东. 渗透检测[M]. 北京:机械工业出版署,2004.
[5] 渗透检测:HB/Z 61-1998[S]. 北京:中国航空工业三〇一研究所出版社,1998.
[6] 李兴卫,张平. 缺陷渗透理论分析[J]. 无损检测,2007,29(12):736-738.
[7] 石振铎. 容器内衬中穿透性缺陷检测[J]. 无损探伤,1997, 16(5):42-45.
[8] 陈崔丽. 轴承用陶瓷球荧光渗透检测[J]. 无损检测,2014, 36(11):59-61.
[9] 王益州. 渗透检测操作的方法和环境对结果的影响[J]. 广州化工,2013,41(15):81.
[10] 苏青风.某型高压涡轮工作叶片的荧光渗透检测工艺改进与细化[J]. 无损探伤,2010,34(3):30-31.
[11] 徐亚亚.某型高压涡轮工作叶片荧光渗透检测工艺改进[J]. 无损探伤,2015,37(9):69-71.
[12] 唐建朝. 某发动机叶片抛修裂纹荧光渗透检测[J]. 无损检测,2014,36(3):72-74.